Magnesium aluminium tubulis ad Inductio ad Brazing
Objective, ut est multimoda aluminium calor 1050 ºF (566 ºC) applicationem ad latinizing:
material:
- Cu tubulis (3/4 "/ 19mm)
- Cu tubulis (5/8 "/ 15.8mm)
- A. tubulis (3/8 "/9.5mm)
- A. varias incideritis (5/8 "/15.8mm)
- A. varias incideritis (3/4 "/19mm)
- Luke Milhaupt-Di-unus mixturae 30 832
- latinize filum
1050 ºF Temperature (566 ºC)
Frequency 260 kHz
UHF apparatu, DW, 10KW 150 calefactio ratio, expeditos in 500 kHz inductionem tractanda est per calorem statione quibus remotis duobus 1.5 μF capacitors.
- In duas partes orbem intentio calidi ovali helical inductione collecta aluminium enucleavimus specie
- A quinque-rursus helical inductione heating coil disposito et AI developed velut fistulae iuncturam C in ecclesia praecipue Brazing
Ize processus: aluminium fistulae fit intentio formae praeexistunt. In positae dein quatuor aluminium tubulis plicia concio inseri anguis. Quod autem succensa erat enim ecclesia 70 circiter minutorum secundorum, ad designandum quod pervenit ad id quod temperatus targeted Latinize aras. Cu nam fistulae quoque forma prior sit disposito braze illis tubulis circumvoluto et comitiis tulere insidet. Quod fuit circa tempus 100 seconds heating exolvuntur. Quidam articulis requiratur ad lignum unum pastum Latinize replete communem totius area Latinize filum ex magnitudine. Si exolvuntur tempus intendatur, cum opus esset lignum unum pascentem, et eliminated.
Results / Benefits: praecisum, iterabilem heating:
- More precise quod client voluit, et non iterabilem heating faces ligavit libera est, quae est inductio possit consequi.
- Temperatus imperium, concedit pro superior temperatus imperium Triticum modi videntur, si referantur ad alia, inter facis usus erat, quam desideravit client