Inductio ad partes Tungsten Carbide Tab Mors Brazing
objective
Inductio ad partes Tungsten Carbide Tab Mors de Brazing
Equipment
DW, UHF 6kW-III-apparatus handheld inductione Brazing
Test 1
materials
• ferro virga, 19.05 mm (0.75 ") OD, ipsi 82.55 mm (3.25") Longitudo
Tungsten Carbide • Text: 38.1 mm (1.5 ") OD, 10.16 mm (0.4") Crassitudo
• Alloy, 19.05 mm (0.75 ") Brazing discs
virtus; kW 4.0
Temperature; Circa DCCIV ° C (F MCCC)
Tempus: VI sec
Test 2
materials
• ferro virga, 12.7 mm (0.50 ") OD, ipsi 76.2 mm (3") Longitudo
Tungsten Carbide • Text: 19.05 mm (0.75 ") OD, 6.35 mm (0.25") Crassitudo
• Alloy, 12.7 mm (0.50 ") Brazing discs
virtus; kW 2.36
Temperature; Circa DCCIV ° C (F MCCC)
Tempus: VI sec
Test 3
materials
• ferro virga, 12.7 mm (0.50 ") OD, ipsi 76.2 mm (3") Longitudo
Tungsten Carbide • Text: I "OD, ipsi 1mm (1.39") Crassitudo
• Alloy, 12.7 mm (0.50 ") Brazing discs
virtus; kW 2.36
Temperature; Circa DCCIV ° C (F MCCC)
Tempus: Sec 20-25 (in tepidi tremerent / off)
Results, et libertate §;
Ferri potest diversis orbis partibus Brazing Carbide inductione una cubet. Virtutis est calor instituta vertendo in quod off switch ad pedem usura a carbide, ne overheating partes.